Synthesis and characterization of fluorine-containing poly-styrene-acrylate latex with core–shell structure using a reactive surfactant |
| Type de document : |
texte imprimé |
| Auteurs : |
Guilong Xu, Auteur ; Lili Deng, Auteur ; Wen Xiufang, Auteur ; Pi Pihui, Auteur ; Dafeng Zheng, Auteur ; Jiang Cheng, Auteur ; Yang Zhuoru, Auteur |
| Année de publication : |
2011 |
| Article en page(s) : |
p. 401-407 |
| Note générale : |
Bibliogr. |
| Langues : |
Américain (ame) |
| Catégories : |
Caractérisation
Copolymère styrène acrylique
Core-Shell
Fluorine
Latex
Surfactants réactifs
|
| Index. décimale : |
667.9 Revêtements et enduits |
| Résumé : |
Fluorine-containing poly-styrene-acrylate (PSA) latex with core–shell structure was successfully synthesized by seeded semicontinuous emulsion polymerization using fluorine monomer Actyflon-G04 and reactive emulsifier DNS-86. The chemical composition, morphology of latex, and surface composition of the latex film were characterized by Fourier transform infrared spectra, transmission electron microscopy, and X-ray photoelectron spectroscopy, respectively. The stability properties of latex were tested by Ca2+, centrifugal and mechanical stability tests, and the latex film was studied by water contact angle, water absorption ratio, and thermo-gravimetric analysis. The results show that fluorine-containing PSA latex particles with crosslinked core and crosslinked shell structure have excellent stability properties, and the film of latex has excellent water repellency, thermal stability, and chemical resistance properties when the amount of fluorine monomer was only 8.0 wt %. |
| Note de contenu : |
- EXPERIMENTAL : Materials - Synthesis of the fluorine-containing PSA latex latex nanoparticles with core-shell structure - Characterization.
- RESULTS AND DISCUSSION : FTIR analysis - Effect of crosslinking - Micromorphology of the core-shell latex nanoparticles - XPS analysis - Stability of the prepared latex - Water repellency and chemical resistance properties of the latex film - Thermal stability of the prepared latex film. |
| DOI : |
10.1007/s11998-010-9308-8 |
| En ligne : |
https://link.springer.com/content/pdf/10.1007%2Fs11998-010-9308-8.pdf |
| Format de la ressource électronique : |
Pdf |
| Permalink : |
https://e-campus.itech.fr/pmb/opac_css/index.php?lvl=notice_display&id=11679 |
in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH > Vol. 8, N° 3 (05/2011) . - p. 401-407
Aller sur edunet
Accueil
Synthesis and characterization of fluorine-containing poly-styrene-acrylate latex with core–shell structure using a reactive surfactant in JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, Vol. 8, N° 3 (05/2011)